FLAME RETARDANT COMPOUND IC-PP35FRP

Physical Property

 

Items Method of experiment Unit Value
Carrier Resin     PP
Flame Retardant Content   % 35
Melting Temperature   0C 160-170
Density ASTM D792 g/cm3 0.92
Melt Flow Index (2300C/2.16kg) ASTM D1238 g/10 min 11.24
Moisture Content ASTM D570 % 0.07
Tensile Strength at Break ASTM D638 MPa 13.67
Tensile Elongation at Break ASTM D638 % 19.46
Flexural Strength ASTM D790 MPa 34.81
Flexural Modulus ASTM D790 MPa 1389.40
Impact Izod Notched ASTM D256 J/m 26.36
Impact Charpy Notched ASTM D6110 KJ/m2 2.52
Hardness Shore D ASTM D2240 D 55.25

Processing Technique                         Injection molding, extrusion

Application Rate                                 100% of the part’s weight

Packing                                                20 kg/bag

Storage                                                 Keep at dry condition