Technical Analysis
| Items | Method of experiment | Unit | Value |
| Carrier Resin | PBT | ||
| Appearance | Natural Pellets | ||
| Glass Fiber Content | % | 30 | |
| Melting Temperature | 0C | 200-220 | |
| Density | ASTM D792 | g/cm3 | 1.29 |
| Melt Flow Index (2500C/5kg) | ASTM D1238 | g/10 min | 5 |
| Moisture Content | ASTM D570 | % | 0.07 |
| Tensile Strength at Break | ASTM D638 | MPa | 80 |
| Tensile Elongation at Break | ASTM D638 | % | 10 |
| Flexural Strength | ASTM D790 | MPa | 90 |
| Flexural Modulus | ASTM D790 | MPa | 5000 |
| Impact Izod Notched | ASTM D256 | J/m | 55 |
Processing Technique Injection molding
Application Rate 100% of the part’s weight based on requirement
Packing 20 kg/bag
Storage Keep at dry condition
IC-PBT300GF is a compound with PBT base resin combined with glass fiber for injection molding. IC-PBT300GF is specially developed for electrical components and equipment applications, products requiring good stiffness, low shrinkage, high dimensional stability.