GLASS FIBER REINFORCED COMPOUND IC-PP300GF

Technical Analysis

Items	Method of experiment	Unit	Value
Carrier Resin			PP
Appearance			Natural Pellets
Glass Fiber Content		%	30
Melting Temperature		0C	150-160
Density	ASTM D792	g/cm3	1.09
Melt Flow Index (2300C/2.16kg)	ASTM D1238	g/10 min	12
Moisture Content	ASTM D570	%	0.05
Tensile Strength at Break	ASTM D638	MPa	60
Tensile Elongation at Break	ASTM D638	%	9
Flexural Strength	ASTM D790	MPa	65
Flexural Modulus	ASTM D790	MPa	4000
Impact Izod Notched	ASTM D256	J/m	55

Processing Technique Injection molding

Application Rate 100% of the part’s weight based on requirement

Packing 20 kg/bag

Storage Keep at dry condition

Description
Reviews (0)

IC-PP300GF is a compound with Polypropylene base resin combined with glass fiber used for injection molding. IC-PP300GF is specially developed for electrical components and equipment applications, products requiring good stiffness, low shrinkage, high dimensional stability.