GLASS FIBER REINFORCED COMPOUND IC-PP300GF

Technical Analysis 

Items  Method of experiment  Unit  Value 
Carrier Resin      PP 
Appearance      Natural Pellets 
Glass Fiber Content    %  30 
Melting Temperature    0C  150-160 
Density  ASTM D792  g/cm3  1.09 
Melt Flow Index (2300C/2.16kg)  ASTM D1238  g/10 min  12 
Moisture Content  ASTM D570  %  0.05 
Tensile Strength at Break  ASTM D638  MPa  60 
Tensile Elongation at Break  ASTM D638  %  9 
Flexural Strength  ASTM D790  MPa  65 
Flexural Modulus  ASTM D790  MPa  4000 
Impact Izod Notched  ASTM D256  J/m  55 

 

Processing Technique                         Injection molding 

Application Rate                                  100% of the part’s weight based on requirement 

Packing                                                 20 kg/bag 

Storage                                                 Keep at dry condition