BIOPOLYMER IC-I9621


BIOPOLYMER IC-I9621

Physical Property 

  Items    Method of experiment  Unit  Standard 
  Carrier Resin      DSC    PBAT 
  Melt Flow Index (190ºC/2.16kg)    ASTMD1238  g/10mins  7 
  Density      ASTM D1895  g/cm3  1.31 
  Melting Temperature    DSC  oC  140-150 
  Moisture Content      ASTM D570  %  1.44 

Properties: 

         
  • Good Processing when dried properly (< 0.1%moisture)
  • Does not produce noxious off gas
  • In-line drying is needed to control moisture which will cause processing issues
  • Good Printability without pre-treatment
  • Good weldability
  • Meets requirements for compostable degradable polymers: DIN EN 13492 and ASTM D6400
  • Bulk storage possible in dry silo

THÔNG TIN SẢN PHẨM

General Description 

IC-I9621 is a biodegradable polymer that may use for injection molding producing heat-resistant articles, such as cutlery, trays, cups, baby toys, etc. After crystallization, IC-I9621 will have excellent heat resistance properties. IC-I9621 can blend with polylactic acid polymer (PLA). It will degrade in the compost environment producing: carbon dioxide, water and biomass. The variety of products made with IC-I9621 is growing every day. Applications include cutlery, cups, plates, cosmetics, and outdoor novelties. 

Processing Information

IC-I9621 biopolymer injection molding applications can be processed on conventional injection molding equipment. The material is stable in the molten state, provided that the drying procedures are followed. Mold flow is highly dependent on melt temperature. It is recommended to balance screw speed, back pressure, and process temperature to control melt temperature. IC-I9621 needs to be process with low moisture content. It is recommended that the moisture level be less than 0.1%.  

Medical Norm 

Attain the Safety Norm for Health and Foodstuff issued by Vietnam Directorate for Standards and Quality allow the decision 3339/2001/QD-BYT promulgated by Vietnam Ministry of Health. Safety apply for handling process. No healthy damage infected. 

Important note: The above values are for reference only and should not be used for specification. These values are intended as a general guide and do not represent any warranty or guarantee of particular performance. 

 

Bình luận

SẢN PHẨM LIÊN QUAN

COMPOUND RESIN CP-HDPE30
General Description  CP-HDPE30 is a type of compound resin containing super fine Calcium Carbonate powder, Polyethylene virgin resin and other additives. It is used directly...
COMPOUND RESIN CP-HIPS30
General Description  CP-HIPS30 is a type of compound resin containing super fine Calcium Carbonate powder, HIPS virgin resin and other additives. It is used directly to cast...
COMPOUND RESIN CP-PE30
General Description  CP-PE30 is a type of compound resin containing super fine Calcium Carbonate powder, Polyethylene virgin resin and other additives. It is used directly to...
BIOPOLYMER IC-I9621
General Description  IC-I9621 is a biodegradable polymer that may use for injection molding producing heat-resistant articles, such as cutlery, trays, cups, baby toys,...
Top
× How can I help you?