Physical Property
| Items | Method of experiment | Unit | Value |
| Carrier Resin | PP | ||
| Appearance | White Pellets | ||
| Glass Fiber Content | % | 18 | |
| Melting Temperature | 0C | 150-160 | |
| Density | ASTM D792 | g/cm3 | 1.12 |
| Melt Flow Index (2300C/2.16kg) | ASTM D1238 | g/10 min | 5.16 |
| Moisture Content | ASTM D570 | % | 0.05 |
| Tensile Strength at Break | ASTM D638 | MPa | 17.93 |
| Tensile Elongation at Break | ASTM D638 | % | 33.06 |
| Flexural Strength | ASTM D790 | MPa | 34.35 |
| Flexural Modulus | ASTM D790 | MPa | 1919.35 |
| Impact Charpy Notched | ASTM D256 | KJ/m2 | 11.86 |
| Hardness Shore D | ASTM D2240 | D | 53 |
Processing Technique Injection molding
Application Rate 100% of the part’s weight
Packing 25 kg/bag
Storage Keep at dry condition
General Description
IC-PP181GF is a compound with PP base resin combined with glass fiber for injection molding. IC-PP181GF has been developed especially for the applications appliances and electrical components, products requiring good rigidity, low shrinkage, high dimensional stability.