COMPOUND SỢI THỦY TINH IC-PBT200GF

 

Technical Analysis 

Items  Method of experiment  Unit  Value 
Carrier Resin      PBT 
Appearance      Natural Pellets 
Glass Fiber Content    %  20 
Melting Temperature    0C  200-220 
Density  ASTM D792  g/cm3  1.25 
Melt Flow Index (2500C/5kg)  ASTM D1238  g/10 min  5 
Moisture Content  ASTM D570  %  0.07 
Tensile Strength at Break  ASTM D638  MPa  70 
Tensile Elongation at Break  ASTM D638  %  10 
Flexural Strength  ASTM D790  MPa  80 
Flexural Modulus  ASTM D790  MPa  4000 
Impact Izod Notched  ASTM D256  J/m  60 

 

Processing Technique                         Injection molding 

Application Rate                                  100% of the part’s weight based on requirement 

Packing                                                 20 kg/bag 

Storage                                                  Keep at dry condition