COMPOUND SỢI THỦY TINH IC-PP400GF

 

 

Items  Method of experiment  Unit  Value 
Carrier Resin      PP 
Appearance      Natural Pellets 
Glass Fiber Content    40 
Melting Temperature    0C  150-160 
Density  ASTM D792  g/cm3  1.11 
Melt Flow Index (2300C/2.16kg)  ASTM D1238  g/10 min  13 
Moisture Content  ASTM D570  0.05 
Tensile Strength at Break  ASTM D638  MPa  70 
Tensile Elongation at Break  ASTM D638 
Flexural Strength  ASTM D790  MPa  75 
Flexural Modulus  ASTM D790  MPa  5000 
Impact Izod Notched  ASTM D256  J/m  50 

 

Processing Technique                         Injection molding 

Application Rate                           100% of the part’s weight based on requirement 

Packing                                       20 kg/bag 

Storage                                       Keep at dry condition